Avoid oil canning on your metal walls with Vitracore G2 panels
HomeHome > News > Avoid oil canning on your metal walls with Vitracore G2 panels

Avoid oil canning on your metal walls with Vitracore G2 panels

May 24, 2023


Metal panels on roofs and walls may appear wavy or distorted, especially in the broad and flat sections. This perceived distortion called oil canning is simply a visual phenomenon characteristic of light-gauge, cold-rolled flat metal products – a cosmetic effect that doesn't impact the structural integrity of the metal panel systems.

Oil canning doesn't discriminate between different metal types – it can occur on aluminium, steel, copper or zinc. The extent of the visual distortion will depend on many factors including the colour, finish, angle of view and even the time of the day.

Oil canning dates back to medieval times when the use of natural metals such as zinc and copper for roofing meant that it was a common feature of the architectural landscape. With advancements in materials and changing aesthetic preferences, buildings are being designed and engineered to achieve a cleaner and streamlined look.

Whilst there are still some within the architectural space who prefer the authentic look of natural metals, many are actively seeking to specify products that will maintain their clean-line aesthetic integrity.

As part of Fairview's commitment to product performance, improvements and innovation, a study was conducted to determine the resistance of Vitracore G2 against forces that would create oil canning.

Fairview's Vitracore G2 is a bonded aluminium panel, with a non-combustible profiled aluminium core, engineered for high performance and unmatched by other metal cladding products.

The analysis was conducted by an external engineer and featured the use of Finite Element Analysis (FEA) software to determine the performance of both G2 and 3mm solid aluminium against oil canning.

In understanding the benchmarks against which the study was conducted, first it is important to detail the known causes and ways to minimise the chances for oil canning, which include:

Stresses during the production process

Oil canning can sometimes occur during the early stages of the coiling production. There are three separate stresses that can be induced on the metal during production that could lead to the development of oil canning:

Stresses during roll forming and slitting:

All metals have a ‘memory’, which sees the material displaying a tendency of ‘trying’ to revert to its original form. The stresses inflicted during roll forming and slitting of the metal coil and sheets can facilitate oil canning as the metal moves and warps in response to metal memory.

Incorrect fastener installation:

There are two common scenarios where oil canning could be attributed to fasteners:

Inadequate space allotted for thermal movement:

Metals expand and contract with heat; therefore, restricting the expansion and contraction needed for proper thermal movement of a metal panel can lead to oil canning. This commonly occurs when panels are double pinned at the edges, which restricts the centres from moving during thermal expansion/ contraction and causes stress on the metal.

Structural changes that put tension on the panels:

Oil canning can also occur when the building experiences a shift in its structure, settles in its foundations, or experiences a force that results in a change in the building envelope from its original form.

The movement in the building needs to be sufficient to induce tension or stress on the metal panels. This influence on oil canning is infrequent but possible if the building is subjected to extreme weathering that can affect the building structure.

Out of plane/ square building structure:

Careful attention should be paid to ensure the substrate that the façade is being installed on is as close to flat and square as possible. Even small values of out of square can lead to problems as most façade cladding spans lengths of up to 4 metres – the longer the span the greater the impact of any out of square on oil canning.

Being a bonded laminate comprising of a profiled aluminium core with an aluminium skin on either side, Fairview's Vitracore G2 offers the best of both worlds. Being half the weight and 50% more rigid compared to the solid aluminium options in the market, Vitracore offers improved performance against the forces that can lead to oil canning.

Using FEA analysis, two scenarios were analysed:

Using the FEA software to add a buckling load that would simulate a load that would bring about an oil canning effect on either panel (referred to as Buckling Factor Ratio). The results being:

In this scenario, Vitracore panel is at a load more than 4 times greater than the buckling mode for the 3mm aluminium panel.

In this scenario, the Vitracore panel is again more than 4 times greater than the buckling mode for the 3mm aluminium panel. Adding stiffeners did not change the result.


This analysis demonstrated the superior performance of Vitracore G2 and specifically:

In addition to Vitracore G2's superior performance, the product provides many benefits, making it the decisive solution to high demand and industry requirements.

The lightweight nature of the panel design helps with installation, reducing overall construction cost, while the almost limitless range of colours and finishes, including the option of customisable graphic panels makes it easy to achieve design intent. Also, G2's comprehensive compliance verification documentation is unmatched by any cladding material in Australia.

Stresses during the production process Stresses during roll forming and slitting: Incorrect fastener installation: Inadequate space allotted for thermal movement: Structural changes that put tension on the panels: Out of plane/ square building structure: Conclusion: